portada Influence of Prosopis Juliflora Wood Flour in Poly Lactic Acid - Developing a Novel Bio-Wood Plastic Composite (en Inglés)
Formato
Libro Físico
Editorial
Idioma
Inglés
N° páginas
40
Encuadernación
Tapa Blanda
Dimensiones
22.9 x 15.2 x 0.2 cm
Peso
0.07 kg.
ISBN13
9781636481197

Influence of Prosopis Juliflora Wood Flour in Poly Lactic Acid - Developing a Novel Bio-Wood Plastic Composite (en Inglés)

Thanneerpanthalpalayam Kandasamy Kannan (Autor) · Rathanasamy Rajasekar (Autor) · Sachin Sumathy Raj (Autor) · Eliva Press · Tapa Blanda

Influence of Prosopis Juliflora Wood Flour in Poly Lactic Acid - Developing a Novel Bio-Wood Plastic Composite (en Inglés) - Kannan, Thanneerpanthalpalayam Kandasamy ; Rajasekar, Rathanasamy ; Raj, Sachin Sumathy

Libro Nuevo

$ 39.510

$ 71.840

Ahorras: $ 32.330

45% descuento
  • Estado: Nuevo
  • Quedan 52 unidades
Origen: Estados Unidos (Costos de importación incluídos en el precio)
Se enviará desde nuestra bodega entre el Viernes 02 de Agosto y el Miércoles 14 de Agosto.
Lo recibirás en cualquier lugar de Chile entre 1 y 3 días hábiles luego del envío.

Reseña del libro "Influence of Prosopis Juliflora Wood Flour in Poly Lactic Acid - Developing a Novel Bio-Wood Plastic Composite (en Inglés)"

A Bio composite comprising Prosopis Juliflora Fiber (PJF) and Poly Lactic Acid (PLA) was processed considering two particulate sized reinforcements, coarse PJF (avg. 15 μm) and fine PJF (10-50 nm). They were added individually at ratios of 10, 15, 20 and 25 wt% into PLA matrix. The composites were extruded and tested for mechanical properties. The addition of PJF resulted with an increase in the tensile, flexural and impact strengths of the polymer. Adding PJF to PLA showed a decrease in the hardness of the polymer. Water Absorption test showed an increase in water uptake with increasing fiber content. The most optimum ratio of PLA to PJF was found to be 80:20. The fine PJF reinforced composites proved to be superior over the coarse PJF reinforced composites at all stages of the research. FESEM and TGA were used to study morphology and thermal characteristics respectively.

Opiniones del libro

Ver más opiniones de clientes
  • 0% (0)
  • 0% (0)
  • 0% (0)
  • 0% (0)
  • 0% (0)

Preguntas frecuentes sobre el libro

Todos los libros de nuestro catálogo son Originales.
El libro está escrito en Inglés.
La encuadernación de esta edición es Tapa Blanda.

Preguntas y respuestas sobre el libro

¿Tienes una pregunta sobre el libro? Inicia sesión para poder agregar tu propia pregunta.

Opiniones sobre Buscalibre

Ver más opiniones de clientes